Hi.
Thank you everyone for the replies. I believe I have found the issue. A part of the clamping system over time shifted and the carbide blade was nicking it. I am guessing it was chipping...
Type: Posts; User: Teldin
Hi.
Thank you everyone for the replies. I believe I have found the issue. A part of the clamping system over time shifted and the carbide blade was nicking it. I am guessing it was chipping...
Hi.
Thank you for the replies.
From what I can see, I don't think the blade is coming to a stop. I have it pretty tight in there, plus I would assume if the arbor was spinning in the blade,...
Hi.
Thank you for your response. The copper is full hard temper, has not gone through any annealing process based on the information from the mill that created the copper. Even though it is full...
Hi. I need assistance with cutting copper alloy C110 that is Full Hard temper.
I have a custom CNC machine with a circular saw blade. I am cutting multiple pieces of copper in a run. The blade...