I don't think it will be, it is more likely to be an epoxy.
Sposl,
I have noticed that with the epoxy I use, if I cure it at a higher temperature, the finished article ends up harder than if it is given a very slow cure. I remember reading about this somewhere. It may only be applicable to certain epoxies.
Shannon.