Cameron -if I spin test samples, they will have directional in their properties, stronger in one direction.
If I do this and send them over, can you produce info that might be useful in comparison to static cast blocks ?
John
Point of interest - what about the aggregate size being restricted to 1/5 minimum dimension ?
This would mean the test samples at 3/8" thick would only have 2mm max particle size ?
Not a problem for me, but what of others ?
Further question to the above - which way up do you test the specimens, with the x-section portrait or landscape ? My specimens will have different values in each direction, I'd guess.
Regards
John