Not sure where to post so will start here. I am making permenant molds for aluminum.
I have had a lot of mold requests that have nasty isolated heavy sections that will require fast cooling . I have been using water cooling in P20 tool steel with good success but always on the bottom of the mold so leaks cannot get into the casting. I have heard of this Anviloy product as being a good heat trandfer product but want to know if it is good for cores and if it can be cooled with a copper cooling jacket on the backside of it. Will this give me a good thermal transfer? Has anyone here used it and what was their success? When using solidification software what would the thermal transfer be so I could use it?
Any help available?
If its not broken you are not trying hard enough